Standard Finishes For Tinnerman Palnut Fasteners Stamped "T" or "D"

 

Standard Finishes For Tinnerman Palnut Fasteners Stamped "T" or "D"

Listed below are the most commonly used finishes available for protective coating and rust-proofing Tinnerman Palnut fasteners and components.

To specify desired finish use corresponding dash number, shown below as the last dash number, affixed to C and D based parts.

Examples: C00183-012 -27, C01053-012-4, or D98334-071M-963.

Click the image below to download the complete Standard Finishes PDF.
STANDARD FINISHES
  Swipe
Finishes for "D" & "T" Stamped Ford GM Daimler Chrysler Description Color Benefits SALT SPRAY
27       Soluble Oil Dipped Ferrous parts (except stainless steel) have a light coating of soluble oil applied. Non-ferrous parts are cleaned where necessary and are left in plain condition. Natural Low-Cost finish, recommended on ferrous parts for conditions of relatively little corrosion or for parts that are to receive a finish in the customers' plants 5% solution at 95 degrees Fahrenheit. Ferrous parts: first rust spots after 1 hour, end point (1/16" dia. rust spots) after 2-1/2 hours. Nonferrous parts: corrosion will be normal for plain finish of the material.
4 ESB-M3P4-A, ESS-MP20-A GM4435 Code A PS80 Plus Oil Phosphate and Oil Parts are phosphate coated, then dipped in a special oil and spun dry Black Moderate corrosion resistance. Neat in appearance -will not wear off in handling. 5% solution at 95 degrees Fahrenheit. First rust spots after 32 hours. End point (1/16" dia. rust spots) after 48 hours.
1   GM4435 Code B PS80, PS85 Phosphate Coated, then Two Coats Olive Drab Paint are applied. Each coat is properly baked to obtain maximum protection. Olive drab. Good corrosion resistance. Does not cause hydrogen embrittlement common with electroplated high carbon spring steel. Excellent for insulating dissimilar metals against electrolytic action. 5% solution at 95 degrees Fahrenheit. First rust spots after 48 hours. End point (1/16" dia. rust spots) after 96 hours.
67   GM4435 Code (093)   Parts are phosphate coated, and then two coats of aluminum paint are applied. Each coat is properly baked to insure maximum protection. Aluminum color- smooth appearance Recommended in place of cadmium plating where appearance and corrosion resistance are requirements. High in abrasion resistance and a non-conductor of electricity. 5% solution at 95 degrees Fahrenheit. First rust spots after 48 hours. End point (1/16" dia. rust spots) after 96 hours.
963 ESAM21P2-A4, WSDM21, P13-A2, A3, WSDM21P11-B1 (S301 for Non-threaded parts) GM6173M PS5873 Water Based zinc coating Dacromat 320 or equivalent plus clear sealer Parts are coated in a water based zinc coating for maximum protection. Grey metallic. Exceptional corrosion resistance. Does not cause hydrogen embrittlement 5% solution at 95 degrees Fahrenheit. End point (1/16" rust spots) after 400 hours.
NOTE: The following electroplate finishes are limited to only a few parts, such as Tubular Type clips and Tube Clamps. Please do not specify these finishes for other types of Tinnerman Palnut fasteners without the approval of our engineering department.
Finishes for "D" & "T" Stamped Ford GM Daimler Chrysler Description Color Benefits SALT SPRAY
600   GM4345M Code 3MU24/0   Zinc Mechanical Plate Parts are mechanically plated from .00015" to .0003" thick. A clear chromate is applied as a sealer. Satin Silver Color. Excellent electrical conductivity and moderate corrosion resistance. No hydrogen embrittlement 5% solution at 95 degrees Fahrenheit. End point (red rust) after 24 hours.
3B     PS4220 Code 15 Zinc Electroplate Parts are zinc electroplated from .00015" to .0002" thick and baked to reduce hydrogen embrittlement. Silver Color. Slight discoloration from baking may occur Excellent electrical conductivity and moderate corrosion resistance 5% solution at 95 degrees Fahrenheit. End point (red rust) after 24 hours.
3963 WSS-M21P36-A2 GM6173 PS-5873P Two coats of water base zinc coating (Geomet) plus one coat geomet "P" clear sealer. Silver Color Exceptional corrosion resistance. Does not cause hydrogen embrittlement and is free of Hexavalent Chrome 5% solution at 95 degrees Fahrenheit. End point (red rust) after 720 Hours
3255 None None None Two coasts of water base zinc coating (Geomet). Silver Color Exceptional corrosion resistance. Does not cause hydrogen embrittlement and is free of Hexavalent Chrome 5% solution at 95 degrees Fahrenheit. End point (red rust) after 330 Hours
3252 S438 & WSS-M21P36-A3 GMW3359   Two coats of water based zinc coating (Geomet) plus two coats of Geoblack 137. Black Exceptional corrosion resistance. Does not cause hydrogen embrittlement and is free of Hexavalent Chrome 5% solution at 95 degrees Fahrenheit. End point (red rust) after 480 Hours